This paper aims to focus on the changes in thermal and surface characteristics of acrylonitrile butadiene styrene (ABS) material when exposed to chemical vapours for surface finishing. The poor surface finish and the dimensional accuracy of the fused deposition modelling parts (of ABS material) because of the stair-stepping hinder their use for rapid tooling applications, which can be improved by vapour finishing process. The differential scanning calorimetry (DSC) tests are performed to investigate the thermal behaviour of ABS thermoplastic after vapour finishing.

The hip prosthesis replica has been used to highlight the efficacy of chemical finishing process for intricate and complex geometries. The replicas are treated with chemical vapours for different durations. The DSC tests are performed along with surface roughness, surface hardness and dimensional measurements of exposed replicas and compared with unexposed replica.

The longer finishing time, i.e. 20 s, manifested higher melting peak temperature, higher melting enthalpy and higher heat capacity along with smoother and harder surface as compared with unexposed replica. The finishing process enhanced the bonding strength and the heat-bearing capacity of ABS material. The vapour finishing process enhanced the thermal stability of the material which may extend its sustainability at higher temperatures.

The improved thermal stability of ABS thermoplastic after chemical vapour finishing has been demonstrated. This advancement allows the use of ABS in functional tooling suitable for small production runs with higher flexibility and lead time savings.

The heat effects associated with phase transitions as a function of temperature are studied in case of replicas finished with chemical vapours. The relationship between melting enthalpy and surface characteristics has been ascertained.

The purpose of this paper is to review the various pre-processing and post-processing approaches used to ameliorate the surface characteristics of fused deposition modelling (FDM)-based acrylonitrile butadiene styrene (ABS) prototypes. FDM being simple and versatile additive manufacturing technique has a calibre to comply with present need of tailor-made and cost-effective products with low cycle time. But the poor surface finish and dimensional accuracy are the primary hurdles ahead the implementation of FDM for rapid casting and tooling applications.

The consequences and scope of FDM pre-processing and post-processing parameters have been studied independently. The comprehensive study includes dominance, limitations, validity and reach of various techniques embraced to improve surface characteristics of ABS parts. The replicas of hip implant are fabricated by maintaining the optimum pre-processing parameters as reviewed, and a case study has been executed to evaluate the capability of vapour smoothing process to enhance surface finish.

The pre-processing techniques are quite deficient when different geometries are required to be manufactured within limited time and required range of surface finish and accuracy. The post-processing techniques of surface finishing, being effective disturbs the dimensional stability and mechanical strength of parts thus incapacitates them for specific applications. The major challenge for FDM is the development of precise, automatic and controlled mass finishing techniques with low cost and time.

The research assessed the feasibility of vapour smoothing technique for surface finishing which can make consistent castings of customized implants at low cost and shorter lead times.

The extensive research regarding surface finish and dimensional accuracy of FDM parts has been collected, and inferences made by study have been used to fabricate replicas to further examine advanced finishing technique of vapour smoothing.

Resistance spot welding (RSW) is an essential process in the automobile sector to join the components. The steel is the principal material utilized in car generation because of its high obstruction against erosion, toughness, ease of support and its recuperation potential. Due to this, it was planned to study the mechanical properties, hardness and microstructure characteristics of RSW of Stainless steel 304.

In the present research, RSW of 304 stainless steel plates with 1 mm thickness and effect of current intensity, welding time, electrode pressure and holding time on nugget diameter, tensile strength microhardness and microstructure of the joints was investigated. The specimens were prepared according to the dimensions of 30 × 100 mm with 30 mm overlaps joint through the RSW machine. The tensile test of the specimen was carried out on a universal testing machine and microhardness of specimens measured using Vickers’s hardness tester. Taguchi L16 orthogonal array was used to scrutinize the significant parameters for each output.

It has been observed that the tensile strength of the specimen is affected by the current intensity and nugget diameter, and the weld time has a significant effect on the tensile strength. Microhardness is highly influenced by electrode pressure and holding time, as the increase in both these parameters resulted in the increase of microhardness. This is due to rapid cooling, which is done by the cooling water flowing through the copper electrodes.

This study was carried out using a copper electrode with a flat face with selected parameters and response factors. The study can be useful for researchers working on optimization of welding parameters on stainless steel.